MANUFACTURERS OF REFRACTORY PRODUCTS   TOTAL REFRACTORY SOLUTION UNDER ONE ROOF,

 
Product MgO (%) (min.) Cr2O3 (%) min SiO2 (%) (max

A.P. (%)max

 C.C.S. hgs/ cm2 min PLC at 1600/ 2 hrs RUL Ta min Thermal Spalling (Air quenching) at 1000 Application
CERA-MAC-I 60 15 - 22 400 -0.5 1600   For general application
CERA-MAV-II 65 10 - 21 450 +_0.5 1600   A.O.D./V.O.D./LRF
CERA-MAV-III 70 8 - 22 400 +_0.5 1600   Alkali resistant brick for paper & chemical industry
CARA-FLEX 82 6 <1 22 500 +_0.5 1700 +100 Cycles For cement plant rotary kiln.
CERA-MAV-D-I 60 12-14 1.0 18 450 _0.5 1750   VOD/AOD slag zone, and copper smelter
CERA-MAV-D-II 65 12-14 2.0 18 450 _0.5 1750   Metal zone of VOD/AOD, bottom,free board
CERA-MAV-D-III 80 5-6 3.0 17 450 _0.5 1750   BOF lining, VOD/AOD/VAD vessel RH.DH vessels
CERA-CM-I 40 18 - 24 300 _0.5 1580   For general application
CERA-CHROME - 40 - 21 500 +/-0.5 1480   Abrasion resistant quality bricks for hearth of soaking pit & reheating furnace
 
 
 
 
Product Setting Sintering tem    Grading (mm) MgO (%) (min.) Cr2O3 (%)
min		 SiO2 (%) (max) Application   Temp Application
CERA-MG-M Ceramic 1550 0-0.5 80-85 - - 1700 For laying of magnesite bricks
CERA-RAM-80 Ceramic 1500 0.5 77-82 - 6.5 1650 For hot & cold repair of steel furnaces
CERA-RAM-80S -do- 1500 0.5 82-84 - 6.0 1700 Same as above,but with better properties
CERA-FET -do- 1500 0.5 77-82 - 6.5 1700 For dry fettling of EAF
CERA-RAM-95 -do- 1550 0.5 92-95 - 2.5 1800 For BOF tap hole ramming
CERA-FILL -do- - 0-10 80 - - 1750 EBT filling mass for EAF
CERA-RAM-D -do- - 0.5 90 - - 1750 Dry ramming mass for EAF bottom
CERA-GUN-B -do- - 0.5 75-80 - 6.5 1750 For repair of EAF Slag zone
CERA-GUN-BS -do- - 0.5 78-84 - 4.0 1750 For repair of EAF slag zone & L.D. converter
CERA-RAM-C 1 -do- 800 0-6 70 8 - 1750 For induction furnace producing SS
CERA-RAM-A 1 -do- 800 0-6 70

15

 - 1750 For induction furnace producing Special Steels
CERA-RAM-M-1 -do- 800 0.8 85 - - 1750 For induction furnace producing Mild steel & Mn steel
 
 